The major causes of broken rails are transverse cracks (often initiating from gauge corner cracks that start at about 70 degrees to the vertical but then 'turn down') and defects at alumino-thermic welds. These defects are difficult to detect reliably using conventional MHz frequency ultrasound propagating typically at angles between the normal to the rail surface and 70 degrees to the vertical. These angles are not well suited to the detection of vertical cracks. There are also problems associated with the geometry of the rail head, severe cracks may be masked by adjacent shallower cracks and it is difficult to penetrate the alumino-thermic weld material. This project is investigating the feasibility of using either low (tens of kHz) or higher frequency guided waves propagating axially along the rail to improve the detection reliability.

Inspection of rail

 

References

Hesse, D. and Cawley, P. 'Surface wave modes in rails', J Acoust Soc Am, Vol 120, pp733-740, 2006.

Hesse, D. and Cawley, P. 'Defect detection in rails using ultrasonic surface waves', Insight, Vol 49, pp318-326, 2007.

Hesse, D. and Cawley, P. 'A single probe spatial averaging technique for guided waves and its application to surface wave rail inspection', IEEE Trans UFFC, Vol 54, pp2344-2356, 2007.

P D Wilcox, M J Evans, B N Pavlakovic, D N Alleyne, K A Vine, P Cawley, M J S Lowe, "Guided wave testing of rail", Insight, vol 45, pp. 413-420, 2003.

P Wilcox, M Evans, O Diligent, M J S Lowe, P Cawley, "Dispersion and excitability of guided acoustic waves in isotropic beams with arbitrary cross-section", Review of Progress in Quantitative NDE, eds. D.O. Thompson and D.E. Chimenti, American Institute of Physics, New York, vol. 21, pp. 203-210, 2002.